Modified Engineering Plastic Material Reinforced PA6

Reinforced PA6 1.High tensile strength 2.Tough resistance,impact resistance Premium 3.Self-lubrication,wear resistance, chemi

Reinforced PA6 

1.Performance

(ITEM)	(UNIT)	(STANDARD)	G10	G20	G30	G30-I	G30-U	G45
Tensile Strength	MPa	ISO 527-2	105	125	170	150	160	195
Tensile Elongation	%	ISO 527-2	3	3	2	3	3	2
Flexural Strength	MPa	ISO 178	165	200	225	210	220	270
Flexural Module	MPa	ISO 178	4000	5500	8000	7000	7800	10000
Charpy Notch Impact	KJ/m2	ISO 179-1	8.5	13	17	30	20	21
Izod Notch Impact	KJ/m2	ISO 180	8	11	18	32	20	22
Mass Density	g/cm3	ISO 1183	1.2	1.28	1.37	1.36	1.37	1.53
H.D.T	°C	ISO 75	190	220	220	215	220	220
Shrinkage For Injection Molding	%	GB/T-15585	0.4-0.8	0.2-0.6	0.2-0.6	0.2-0.6	0.2-0.6	0.2-0.5
Characteristics			General	General	General	Impact resistance	Hydrolysis	High rigidity

2. Glass fiber reinforced PA6    Nylon glass fiber, the rigidity, heat resistance, aging resistance is obviously improved, creep, water absorption and shrinkage decreases, the surface hardness and wear resistance increase was mainly non-ferrous metals used in place of the engine hood, door Handles and other automobile parts, industrial gear, power tools housing, coil skeleton, railway equipment, fishing gear, electrical and electronic connectors and other fields.

3.Recommended processing conditions:

Drying temperature :80-100 ,3-4HFeeding section: 200 ~ 210 °C the middle section: 250 ~ 290 °C nozzle section: 250 ~ 280 °CInjection pressure of 70 ~ 120MPaHolding pressure 40 ~ 80 MpaMold temperature 70 ~ 100 °CBack pressure 0 ~ 10 Mpa