Glassfiber reinforced PP

Glassfiber reinforced PP 1.Impact resistance 2.High rigidity 3.Drying temperature :90-100

Glassfiber reinforced PP

1. Performance

(ITEM)	(UNIT)	(STANDARD)	G15	G20	G30	G40	G30-B	G30-I
Tensile Strength	MPa	ISO 527-2	60	70	80	85	70	55
Tensile Elongation	%	ISO 527-2	-	-	-	-	-	-
Flexural Strength	MPa	ISO 178	85	90	105	110	95	70
Flexural Module	MPa	ISO 178	3500	4800	5500	6000	5000	4000
Charpy Notch Impact	KJ/m2	ISO 179-1	9.5	11	15	15	22	40
Izod Notch Impact	KJ/m2	ISO 180	7	9.5	13.5	13	20	36
Mass Density	g/cm3	ISO 1183	0.99	1.03	1.12	1.23	1.12	1.1
H.D.T	°C	ISO 75	130	145	150	150	145	135
Shrinkage For Injection Molding	%	GB/T-15585	0.7-1.0	0.5-0.8	0.5-0.8	0.5-0.8	0.5-0.8	0.5-0.8
Characteristics			General	General	General	High rigidity	Impact resistance	Impact resistance

2.Recommended processing conditions

Drying temperature :90-100 ,2-4HFeeding section: 200 ~ 210 °C the middle section: 210 ~ 240 °C nozzle section: 210 ~ 230 °CInjection pressure of 50 ~ 80MPaHolding pressure 40 ~ 60 MpaMold temperature 30 ~ 60 °CBack pressure 5 ~ 10 Mpa

3.Enhanced PP

    PP can be enhanced substantially increase the tensile strength, stiffness, hardness and heat resistance, reduce mold shrinkage and linear expansion coefficient, and maintain a good chemical resistance of PP, the price is relatively low, can be used as engineering plastics. Main use: widely used in the automotive industry, car manufacturing before the guard, after the car hood, heater housing, etc.; for the electrical industry, manufacturing, instrument case, battery boxes, etc.; for the chemical industry, manufacture of metering pumps, corrosion-resistant pipe Road, and frame filter shell. Provides low temperature grade and high flow grade

Glassfiber reinforced PP